Vacuum Bagging Film For Composite Material Carbon Fiber Fabric Fiberglass Cloth Infusion Forming Moulding Process

Vacuum Bagging Film For Composite Material Carbon Fiber Fabric Fiberglass Cloth Infusion and Forming Moulding Process

Details:

vacuum bag membrane is a copolymer film. It has good extensibility, barrier air and automatic demoulding, so it can be directly contacted with resin, mainly for composite material at room temperature molding, vacuum guiding and pre compaction.

technical parameter
Raw material: PA+PE+PA
Color: yellow
Thickness: 0.065mm

Width: 4 meters and 6 meters

Maximum use temperature: 170 degrees centigrade
Elongation (%): longitudinal 450 + 10% transverse 460 + 10%
Tensile strength / (Mpa): longitudinal 450 + 10% transverse 460 + 10%
Anti puncture: 1.2N

Operation Instructions:
1. should avoid the sharp object as far as possible.
2. operation to ensure the surface of the product surface water, no oil stains.